Enhanced interface adhesion by novel eco-epoxy adhesives based on the modified tannic acid on al and CFRP adherends

Abstract

This paper presents a new process for obtaining eco-epoxide adhesives synthesized from bio-renewable raw material (tannic acid-TA) and used for bonding lightweight materials (aluminum (Al) and carbon fiber reinforced polymer (CFRP). Two synthesized bio-epoxy components based on TA, (A) glycidyl ether and (B) glycidyl phosphate ester of TA, were used as a replacement for the toxic epoxy component based on Bisphenol A. The effect of eco-epoxy components on the interface adhesion was measured by the determination of adhesion parameter b, which was compared to the reference epoxy (REF). The increase of adhesion parameter b was 77.5% for A and 151.5% for B. The adhesion of both eco-adhesives was tested using the bell peel test (BPT) with the Al and CFRP adherends. When compared to REF, the average peel load for B was 17.6% (39.3%) and 58.3% (176.9%) higher for the Al and CFRP adherends, respectively. Complete adhesion failure of REF reflected the weak adhesion to both Al and CFRP, which was improved by the addition of eco-epoxy components A and B showing the presence of cohesive failure. The microhardness testing method of interface adhesion was proven to be a fast and reliable testing method, providing a qualitative indication in adhesive selection.

Sofia Teixeira de Freitas

Principal Investigator

Sofia Teixeira de Freitas researches the structural integrity of bonded and layered materials to enable durable, sustainable structures. She is also an accredited group facilitator, committed to building academic environments grounded in cooperation and inclusion—key to overcoming technological limits and addressing the challenges of a truly sustainable society.